Abstract Graphene oxide (GO) was electropolymerized with polyaniline (PANI) during graphite exfoliation in 0.1 M H2SO4 electrolyte and 0.1 M aniline monomer solution. Characterization techniques, including Infrared Absorption Spectroscopy (FTIR), Thermogravimetric Analysis (TGA), UV-vis spectroscopy, X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and cyclic voltammetry, were utilized. XRD analysis confirmed GO multilayer exfoliation from the graphite anode, while UV-vis and FTIR techniques confirmed PANI electropolymerization. SEM images revealed PANI distributed between GO multilayers with a nanoneedle morphology. Cyclic voltammetry in 1 M H2SO4 demonstrated that the GO/PANI composite achieved a specific capacitance of 117.440 Fg-1, in contrast to GO's 1.243 Fg-1, both at a scan rate of 1 mVs-1. This enhancement is attributed to the improved electrical conductivity from PANI and graphene oxide. These results highlight the potential of the GO/PANI composite for high-performance supercapacitors and energy storage systems.

Abstract In this paper, we report the synthesis and evaluation of a poly(vinyl alcohol)/poly(glycerol) dendrimer hydrogel incorporated with green synthesized silver nanoparticles (PVA/PGLD-AgNPs) using Cinnamomum verum extract as the reducting agent (Cz-extract). The Cz-extract was prepared using ultrasonic technique. UV-visible (UV-vis) spectra of Cz-extract confirmed the presence of cinnamaldehyde. PVA/PGLD-AgNPs films were prepared using 5, 10 and 20 mL of Cz-extract and characterized by UV-vis, Fourier transform infrared spectroscopy, Thermogravimetric analysis and X-ray diffraction (XRD). The surface plasmon resonance band in the UV-vis spectra confirmed the formation of AgNPs. XRD pattern confirmed the presence of silver, with average crystallite sizes calculated by Scherrer equal to 13.64 nm, 16.63nm and 20.27 nm for AgNPs prepared with 5 mL, 10 mL and 20 mL of Cz-extract, respectively. AgNPs release kinetic was studied by Korsmeyer- Peppas model. The antimicrobial results revealed that the PVA/PGLD-AgNPs hydrogels showed good antibacterial activity behavior against Escherichia coli.